Borealis FT5236 Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis FT5236 Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FT5236 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Includes anti-block, antioxidant and medium slip additives. Applications FT5236 has been developed especially for applications like: carrier-bag film, pouches, lamination films, and food packaging.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ISO 1183
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Antiblock Level 800 ppm
800 ppm
synthetic silica; Borealis Method
Slip Level 550 ppm
550 ppm
erucamide; Borealis Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 250 %
250 %
ISO 527-3
Film Elongation at Break, TD 550 %
550 %
ISO 527-3
Tensile Modulus 0.230 GPa
33.4 ksi
MD; ASTM D882-A
0.260 GPa
37.7 ksi
TD; ASTM D882-A
Puncture Energy 2.50 J
1.84 ft-lb
66N; ASTM D5748
Coefficient of Friction 0.20
0.20
Dynamic; ISO 8295
Elmendorf Tear Strength, MD 10.19 g/micron
258.8 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 5.097 g/micron
129.5 g/mil
ISO 6383/2
Dart Drop Test 120 g

@Thickness 0.0400 mm
0.265 lb

@Thickness 0.00157 in
ISO 7765-1
Film Tensile Strength at Break, MD 27.0 MPa
3920 psi
ISO 527-3
Film Tensile Strength at Break, TD 24.0 MPa
3480 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 112 °C
234 °F
ISO 11357-3
Vicat Softening Point 97.0 °C
207 °F
ISO 306
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM D1003
Gloss 85 %
85 %
ASTM D2457