Borealis LE6023 Polyethylene Modified Jacketing Compound

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis LE6023 Polyethylene Modified Jacketing Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE6023 is a black flexible low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low temperature performance in combination with good extrudability. LE6023 contains 2.5% well dispersed furnace black of nominal particle size less than 25 nanometers in order to ensure excellent weathering resistance. Applications: LE6023 is designed for jacketing of energy and communication cables. Specifications: ASTM D1248 Type I, Class C, Category 4; IEC 60502, Type ST3; IEC 60708; IEC 60840, Type ST3; and ISO 1872-PE, KCHL, 23-D003.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
base resin; ISO 1183
0.934 g/cc
0.0337 lb/in³
compound; ISO 1183
Environmental Stress Crack Resistance >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
Igepal 100%; F20; IEC 60811-4-1/B
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 45
45
1s; ISO 868
Tensile Strength at Break >= 14.0 MPa
>= 2030 psi
50mm/min; ISO 527
Elongation at Break >= 600 %
>= 600 %
50m/min; ISO 527
Flexural Modulus 0.125 GPa
18.1 ksi
ISO 178
Thermal Properties Metric English Comments
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+6 ohm-cm
1.00e+6 ohm-cm
DC; IEC 60093
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
2.5

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 20.0 kV/mm
508 kV/in
IEC 60243
Dissipation Factor 0.0060

@Frequency 1.00e+6 Hz
0.0060

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Processing Temperature 80.0 - 100 °C
176 - 212 °F
conductor preheating temperature
Melt Temperature 200 - 210 °C
392 - 410 °F