Chosun Refractories MMCT-75 Special Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories MMCT-75 Special Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.006867 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
0.9960 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.00981 GPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
1.42 ksi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| 0.01962 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
2.846 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 34.3 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
4980 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 58.8 MPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
8530 psi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 88.3 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
12800 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.150 % <br>@Temperature 1350 °C,<br> Time 10800 sec |
-0.150 % <br>@Temperature 2460 °F,<br> Time 3.00 hour |
|
| -0.0600 % <br>@Temperature 110 °C,<br> Time 86400 sec |
-0.0600 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
||
| 0.30 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.30 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 75 % | 75 % | |
| SiO2 | 10 % | 10 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Vibrating | |
| Material Required for Estimating(kg/?) | 2,500 | |
| Water Required for Casting(%) | 8.0 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/BK Polyamide 66, with glass fiber and PTFE
- SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66
- Techmer ES Electrafil® DB-1200/S/7/FR ABS, 7% Stainless Steel Fiber Reinforced (dry blend), Flame Retardant
- Styrolution Terblend® N NM-19 ABS/PA6 (Dry)
- Polyram RamLloy PJ702 ASA & ABS Alloy
- Eagle Brass 305 Austenitic Stainless Steel, 1/2 Hardened
- Braskem Prisma 2400 RACO Random Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved