- Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade
Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2035 Linear Low Density Polyethylene, Cast Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2035 Polyethylene resin is for cast film extrusion. It offers excellent tear strength, toughness and good processability. It complies with FDA regulation 21 CFR 177.1520(c) 3.2a when used unmodified and according to good manufacturing practices for food contact applications. It has been approved by USDA for packaging meat and poultry products.Film properties below based on a film thickness of 30 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg |
6.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 7.6. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 15.9 MPa | 2310 psi | Molded property |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | |
| Film Tensile Strength at Yield, TD | 8.30 MPa | 1200 psi | |
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | Molded property |
| Film Elongation at Break, MD | 660 % | 660 % | |
| Film Elongation at Break, TD | 800 % | 800 % | |
| Elongation at Break | 770 % | 770 % | Molded value |
| Modulus of Elasticity | 0.0110 GPa | 1.60 ksi | Molded sample |
| 0.255 GPa | 37.0 ksi | 2% secant modulus | |
| Elmendorf Tear Strength MD | 300 g | 300 g | |
| Elmendorf Tear Strength TD | 540 g | 540 g | |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | |
| Dart Drop | 4.00 g/micron | 102 g/mil | |
| Film Tensile Strength at Break, MD | 46.2 MPa | 6700 psi | |
| Film Tensile Strength at Break, TD | 33.8 MPa | 4900 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 97.2 °C | 207 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.3 % | 1.3 % | |
| Gloss | 95 % | 95 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |