Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Eastman 184MF Polyethylene Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman 184MF Polyethylene Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyethylene 184MF is a low-density formulation with medium slip and low antiblock. It is suggested for film applications where enhanced processability and high clarity are required. It is characterized by good tear strength, impact strength, wide heat-sealing range and printability. An additive in this formulation limits the use of 184MF to nonalcoholic foods, and the average thickness of such polymers in the form in which they contact food shall not exceed 0.0050 inch.Applications/UsesFood packagingHousehold wrapsHousehold bagsEastman Chemical Company sold its polyethylene business to Westlake Chemical Corporation in Dec. 2006. This grade no longer appears in the Westlake product line.
Physical Properties Metric English Comments
Base Resin Density 0.921 g/cc
0.0333 lb/in³
ASTM D4883
Water Vapor Transmission 18.6 g/m²/day
1.20 g/100 in²/day
ASTM F372
Oxygen Transmission 200 cc-mm/m²-24hr-atm
508 cc-mil/100 in²-24hr-atm
ASTM D3985
Thickness 31.75 microns
1.250 mil
Base Resin Melt Index 2.5 g/10 min
2.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 24.0 MPa
3480 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Secant Modulus, MD 0.172 GPa
24.9 ksi
0.01; ASTM D882
Secant Modulus, TD 0.193 GPa
28.0 ksi
0.01; ASTM D882
Coefficient of Friction 0.25
0.25
ASTM D1894
Elmendorf Tear Strength, MD 10.08 g/micron
256.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.35 g/micron
136 g/mil
ASTM D1922
Dart Drop 2.36 g/micron
59.9 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 20.0 MPa
2900 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 94.0 °C
201 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.5 %
4.5 %
ASTM D1003
Gloss 75 %
75 %
at 45°; ASTM D2457
Transmission, Visible 50 %
50 %
Transparency; ASTM D1746