ExxonMobil Escorene® HDZ-128 MMW-HDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® HDZ-128 MMW-HDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.Can be processed on high stalk, pocket extrusion or cast lines. Films made from HDZ-128 exhibit an excellent stiffness balance. High thermal stability provides excellent film appearance and high quality recycle.Applications: Oriented film products; Protective packaging; Deli wrap; Specialty packaging. Data for film properties below based on 1 mil film.
Physical Properties Metric English Comments
Density 0.958 g/cc
0.0346 lb/in³
Exxon Method
Thickness 25.4 microns
1.00 mil
Melt Flow 0.45 g/10 min
0.45 g/10 min
Exxon Method (I2). HLMI (I21) is 30 g/10 min.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 32.0 MPa
4640 psi
ASTM D882
Film Tensile Strength at Yield, TD 26.0 MPa
3770 psi
ASTM D882
Elongation at Break 410 %
410 %
ASTM D638
Secant Modulus, MD 1.15 GPa
167 ksi
ASTM D882
Secant Modulus, TD 1.70 GPa
247 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.433 g/micron
11.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 28.0 g/micron
710 g/mil
ASTM D1922
Dart Drop <= 1.46 g/micron
<= 37.0 g/mil
F50; ASTM D1709
Film Tensile Strength at Break, MD 72.0 MPa
10400 psi
ASTM D882
Film Tensile Strength at Break, TD 36.0 MPa
5220 psi
ASTM D882