ExxonMobil LD 637.LI Molding, Extrusion and Compounding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Molded
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 637.LI Molding, Extrusion and Compounding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 637.LI is a high melt index LDPE homopolymer intended for injection molding or compounding applications requiring high flow. It is ideal for tamper-evident, tear-to-open closures. It can also be used in compounds and concentrates.Availability: Latin America, North America and South AmericaAdditive: Antiblock: NoSlip: 550 ppmThermal Stabilizer: NoApplications: CapsClosuresCompounding Injection Molding Masterbatch Base ResinViscosity Modifier Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.922 g/cc	0.0333 lb/in³	ExxonMobil Method
Melt Flow	40 g/10 min @Load 2.16 kg, Temperature 190 °C	40 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Slip Level	550 ppm	550 ppm

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	88	88	15s; ASTM D2240
Hardness, Shore D	43	43	15s; ASTM D2240
Tensile Strength at Break	7.58 MPa	1100 psi	ASTM D638
Tensile Strength, Yield	12.4 MPa	1800 psi	ASTM D638
Elongation at Break	110 %	110 %	ASTM D638
Elongation at Yield	30 %	30 %	ASTM D638
1% Secant Modulus	276 MPa	40100 psi	ASTM D790
Impact Test	19.0 J	14.0 ft-lb	@ 73ºF, Instrumented Impact Total Energy; ASTM D3763
	21.7 J @Temperature 0.000 °C	16.0 ft-lb @Temperature 32.0 °F	Instrumented Impact Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	105 °C	221 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	86.1 °C	187 °F	ASTM D1525