Ineos Nova Zyntar® F7080UV Developmental Flame Retardant Polystyrene  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Nova Zyntar® F7080UV Developmental Flame Retardant Polystyrene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: General purpose non-Deca based resin (does not combine with Decabromodiphenyloxide)Good indoor UV light color stability(grey colors)UL94 V-0 @ 1.5 mm for all colors Good aesthetics for injection molding Applications: Television cabinetsConsumer electronicsBusiness equipmentInformation provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. 
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm
0.0030 - 0.0070 in/in
ASTM D955
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 200 °C
10 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Condition G; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 24.1 MPa
3500 psi
ASTM D638
Elongation at Break 40 %
40 %
ASTM D638
Flexural Strength 44.0 MPa
6380 psi
ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
ASTM D790
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Processing Properties Metric English Comments
Rear Barrel Temperature 171 - 193 °C
340 - 379 °F
Middle Barrel Temperature 199 - 221 °C
390 - 430 °F
Front Barrel Temperature 210 - 232 °C
410 - 450 °F
Melt Temperature 210 - 232 °C
410 - 450 °F
Mold Temperature 32.0 - 54.0 °C
89.6 - 129 °F
Back Pressure 0.345 MPa
50.0 psi