Ipiranga Petrochem LTH 0212 LLDP

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Ipiranga Petrochem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ipiranga Petrochem LTH 0212 LLDP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and bags.IPQ employs Spherilene technology from Montell/Italy in the production of LLDPE. The raw materials, which are supplied by COPESUL, are pre-treated and fed into gas-phase reactors, where linear low density polyethylene globe-shaped grains are obtained. These grains are sent to the extrusion site, where stabilizers are added to them. The grains are turned into pellets by an extruding press. Next, they are sent to storage silos, and then to the packaging site. This technology uses state-of-the-art techniques to control the entire production process, thus ensuring the quality of the products that are marketed. Applications:stretch cast film for automatic and manual packing
Physical Properties Metric English Comments
Density 0.910 g/cc
0.0329 lb/in³
ASTM D1505-98
Melt Flow 1.6 - 2.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 - 2.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238-00
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.80 MPa
1420 psi
ASTM D882-02
Film Tensile Strength at Yield, TD 9.60 MPa
1390 psi
ASTM D882-02
Film Elongation at Break, MD 690 %
690 %
ASTM D882-02
Film Elongation at Break, TD 870 %
870 %
ASTM D882-02
Film Elongation at Yield, MD 43 %
43 %
ASTM D882-02
Film Elongation at Yield, TD 36 %
36 %
ASTM D882-02
Coefficient of Friction >= 1.0
>= 1.0
ASTM D1894-99
Dart Drop Test 250 g
0.551 lb
ASTM D1709-98
Film Tensile Strength at Break, MD 52.0 MPa
7540 psi
ASTM D882-02
Film Tensile Strength at Break, TD 47.0 MPa
6820 psi
ASTM D882-02
Optical Properties Metric English Comments
Haze 2.2 %
2.2 %
ASTM D1003A-00
Gloss 81 %
81 %
ASTM D785-03