LATI Latilub 73/13-10T Y/15 POM, 15% Aramid Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Aramid Fiber Filled , Acetal Copolymer, PTFE Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 73/13-10T Y/15 POM, 15% Aramid Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyoxymethylene (POM). PTFE. Aramid fibersAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
Linear Mold Shrinkage, Flow 0.0155 - 0.019 cm/cm
0.0155 - 0.019 in/in
Linear Mold Shrinkage, Transverse 0.0165 - 0.020 cm/cm
0.0165 - 0.020 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
Elongation at Break 6.0 %
6.0 %
Elongation at Yield 4.5 %
4.5 %
Tensile Modulus 3.30 GPa
479 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Coefficient of Friction, Dynamic 0.13
0.13
Coefficient of Friction, Static 0.18
0.18
K (wear) Factor 3.90 x 10-8 mm³/N-M
1.94 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Vicat Softening Point 140 °C

@Load 5.00 kg
284 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 175 - 200 °C
347 - 392 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Copyright © lookpolymers.com All Rights Reserved