LATI Latilub 80-17ST G/30 PPS, 30% Glass Fiber Reinforced, Silicone/PTFE Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 80-17ST G/30 PPS, 30% Glass Fiber Reinforced, Silicone/PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyphenylene Sulfide (PPS). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.67 g/cc
0.0603 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0040 cm/cm
0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 135 MPa
19600 psi
Elongation at Break 1.7 %
1.7 %
Tensile Modulus 11.0 GPa
1600 ksi
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Coefficient of Friction, Dynamic 0.16
0.16
Coefficient of Friction, Static 0.19
0.19
K (wear) Factor 8.50 x 10-8 mm³/N-M
4.22 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 275 °C
527 °F
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
491 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 150 °C
266 - 302 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa