LG Chemical LUTENE FB0800 LDPE Blown Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE FB0800 LDPE Blown Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE FB0800 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of greenhouse film. LUTENE FB0800 have the excellent mechanical properties and optical properties make suitable for manufacture of greenhouse films. (LUTENE FB0800 contains slip agent andMain Application: Greenhouse, tunnel film, filmCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 |
| Water Vapor Transmission | 12.0 g/m²/day | 0.773 g/100 in²/day | |
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM D1922 |
| Dart Drop Test | 230 g | 0.507 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.7 MPa | 3150 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | DSC |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 - 200 °C | 338 - 392 °F | |
| Blow-up Ratio (BUR) | 1.5 - 2.0 | 1.5 - 2.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Slip Coefficient | 0.15 | ASMT D1894 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 52A
- Lucent Polymers TPP-320 Polypropylene, 20% Talc Filled, Impact Modified
- Karina CAK 65-48/1-F Black PVC Compound
- SABIC Innovative Plastics LNP Lubricomp KFL34 Acetal Copolymer (Europe-Africa-Middle East)
- Shandong Dongyue Polymer DF-204 PTFE Fine Powder
- Epoxy Technology EPO-TEK® H20E-PFC Electrically Conductive, Silver Epoxy
- Chosun Refractories MSM-40 High-Adhesion Mortar
- CMW® THERMKON® 70M Molybdenum Copper parts
Copyright © lookpolymers.com All Rights Reserved