Lehmann & Voss LUVOCOM® 65-8498 PP-copolymer, unreinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Lehmann & Voss & Co.
Trade Name LUVOCOM®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss LUVOCOM® 65-8498 PP-copolymer, unreinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Office communication.Reduced moment of inertia compared with metal parts.Dynamic stressed parts.Especially suitable for thin wall complex parts.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
ISO 1183
Water Absorption <= 0.10 %
<= 0.10 %
23°C/24h
Linear Mold Shrinkage 0.015 - 0.030 cm/cm
0.015 - 0.030 in/in
Mechanical Properties Metric English Comments
Tensile Stress 20.0 MPa
2900 psi
Elongation at Yield 3.0 %
3.0 %
3.6 %
3.6 %
flexural
Modulus of Elasticity 2.00 GPa
290 ksi
Flexural Strength 30.0 MPa
4350 psi
Flexural Modulus 3.00 GPa
435 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
edgewise; ISO 179 1eU
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
110 °C
230 °F
short term
Vicat Softening Point 80.0 °C
176 °F
DIN ISO 306
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+9 ohm
>= 1.00e+9 ohm
Insulation Resistance >= 1.00e+9 ohm
>= 1.00e+9 ohm
Processing Properties Metric English Comments
Processing Temperature 230 - 260 °C
446 - 500 °F
mass temp
Nozzle Temperature 220 - 250 °C
428 - 482 °F
Zone 1 220 - 250 °C
428 - 482 °F
Zone 2 220 - 250 °C
428 - 482 °F
Zone 3 230 - 260 °C
446 - 500 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 70.0 - 95.0 °C

@Time 7200 - 14400 sec
158 - 203 °F

@Time 2.00 - 4.00 hour
Dehumidifying dryer
Descriptive Properties Value Comments
Color natural color (black)