LyondellBasell Petrothene® LP540200 High Density Polyethylene, Film Extrusion Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® LP540200 High Density Polyethylene, Film Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PETROTHENE LP540200 is a copolymer resin designed for blown film applications. This resin offers high ESCR, stiffness, excellent appearance and bubble stability. LP540200 is recommended for high strength multi-wall sack liners and barrier sheeting. It is also useful as a blend component for improved stiffness and machinability.Regulatory Status: LP540200 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ASTM D1505
Water Vapor Transmission 5.10 g/m²/day
0.328 g/100 in²/day
ASTM F372
Oxygen Transmission Rate 2450 cc/m²/day
158 cc/100 in²/day
ASTM D3965
ESCR 100% Igepal® >= 1000 hour
>= 1000 hour
molding; ASTM D1693
Thickness 50.8 microns
2.00 mil
Melt Flow 0.17 g/10 min
0.17 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
molding; ASTM D2240
Film Tensile Strength at Yield, MD 19.3 MPa
2800 psi
ASTM D882
Film Tensile Strength at Yield, TD 228 MPa
33000 psi
ASTM D882
Tensile Strength, Yield 21.9 MPa
3180 psi
molding; ASTM D638
Film Elongation at Break, MD 510 %
510 %
ASTM D882
Film Elongation at Break, TD 680 %
680 %
ASTM D882
Elmendorf Tear Strength MD 40 g
40 g
ASTM D1922
Elmendorf Tear Strength TD 1150 g
1150 g
ASTM D1922
Dart Drop 1.38 g/micron
35.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 46.9 MPa
6800 psi
ASTM D882
Film Tensile Strength at Break, TD 29.6 MPa
4300 psi
ASTM D882
1% Secant Modulus, MD 565 MPa
82000 psi
ASTM E111
1% Secant Modulus, TD 758 MPa
110000 psi
ASTM E111
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 64.0 °C
147 °F
molding; ASTM D648
Vicat Softening Point 119 °C
246 °F
ASTM D1525
Brittleness Temperature <= -76.0 °C
<= -105 °F
molding; ASTM D746
Processing Properties Metric English Comments
Melt Temperature 210 - 221 °C
410 - 430 °F
Die Opening 0.1524 cm
0.06000 in
Blow-up Ratio (BUR) 2.5
2.5