MRC Polymers MAXTELâ„¢ 600-BK TPO, Black

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO)
Manufacturer MRC Polymers
Trade Name MAXTEL™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF MRC Polymers MAXTELâ„¢ 600-BK TPO, Black.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
For automotive exterior applications. Excellent process ability and dimensional stability.Unfilled TPOAvailable in black and gray onlyCan be UV StabilizedInternal and external lubricants can be addedInformation provided by MRC Polymers Inc.
Physical Properties Metric English Comments
Specific Gravity 0.980 g/cc
0.980 g/cc
ISO 1183
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 230 °C
17 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 58
58
15sec dwell; ISO 868
Tensile Strength, Yield 16.0 MPa
2320 psi
ISO 527
Flexural Strength 22.0 MPa
3190 psi
ISO 178
Flexural Modulus 1.05 GPa
152 ksi
ISO 178
Izod Impact, Notched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C

@Thickness 3.17 mm
149 °F

@Thickness 0.125 in
un-annealed; ISO 75
Processing Properties Metric English Comments
Rear Barrel Temperature 182 - 204 °C
360 - 400 °F
Middle Barrel Temperature 193 - 216 °C
380 - 420 °F
Front Barrel Temperature 204 - 227 °C
400 - 440 °F
Nozzle Temperature 216 - 238 °C
420 - 460 °F
Melt Temperature 221 - 243 °C
430 - 470 °F
Mold Temperature 21.1 - 32.2 °C
70.0 - 90.0 °F
Drying Temperature 48.9 - 65.6 °C
120 - 150 °F
Usually not required
Dry Time 1 - 2 hour
1 - 2 hour
Injection Pressure 48.3 - 55.2 MPa
7000 - 8000 psi
Back Pressure 0.000 - 1.03 MPa
0.000 - 150 psi
Cushion 0.635 cm
0.250 in
Descriptive Properties Value Comments
Fill Rate Slow to Moderate
Screw Speed Slow to Moderate