Old Hickory M&M Clays, Inc. Wilco-SLU Kaolin Clay

Category Ceramic , Clay , Kaolin Clay
Manufacturer Old Hickory Clay Co.
Trade Name M&M Clays, Inc.
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Old Hickory M&M Clays, Inc. Wilco-SLU Kaolin Clay.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Wilco SLU is an aqueous suspension of kaolin produced at 70% solids content. The slurry is deflocculated and rheology stabilized with sodium silicate. The Wilco SLU grade is a highly permeable selection and recognized for its coarse particle size distribution. In a ceramic casting formulation, it offers fast casting rate for reduced casting times and quick firming of the piece upon drainage of the mold and removal of the piece for drying.Information provided by Old Hickory Clay Company
Physical Properties Metric English Comments
Specific Gravity 1.76 g/cc
1.76 g/cc
Bulk Density 1.76 g/cc
0.0636 lb/in³
Moisture Absorption <= 30.0 %
<= 30.0 %
Particle Size 0.50 µm
0.50 µm
24.4% of particles less than
1.0 µm
1.0 µm
37.4% of particles less than
2.0 µm
2.0 µm
49.2% of particles less than
2.1 µm
2.1 µm
Median particle diameter
5.0 µm
5.0 µm
71.2% of particles less than
10 µm
10 µm
87.4% of particles less than
<= 20 µm
<= 20 µm
96.2% of particles less than
pH 5.0 - 7.0
5.0 - 7.0
10% solids
Specific Surface Area 10 m²/g
10 m²/g
Brookfield Viscosity 250 cP
250 cP
70% solids dispersed using a Brookfield #3 spindle at 100 rpm
Component Elements Properties Metric English Comments
Al2O3 38.21 %
38.21 %
CaO 0.040 %
0.040 %
Fe2O3 0.36 %
0.36 %
K2O 0.11 %
0.11 %
Loss on Ignition(%) 13.51 %
13.51 %
MgO 0.020 %
0.020 %
Na2O 0.020 %
0.020 %
SiO2 45.16 %
45.16 %
TiO2 1.77 %
1.77 %
Descriptive Properties Value Comments
Casting Rate (Barold) 120
CEC/MBI (meg/100 ml) 2
Pyrometric Cone Equivalent (PCE) 34
Wet Sieve Residue (%) 2
Wet Sieve Residue, +325 mesh