Plastcom PLASTAMID® 66 BT B 27 A/IM PA66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	Plastcom spol. s r.o.
Trade Name	PLASTAMID®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastcom PLASTAMID® 66 BT B 27 A/IM PA66.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Basic type PA66 for injection molding, modified for general use, with excellent manufacturing properties. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, hobby tools, toys. Delivered in the black mode.Information Provided by Plastcom spol. s r.o.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	STN EN ISO 1183-1
Melt Flow	9.0 g/10 min @Load 0.325 kg, Temperature 275 °C	9.0 g/10 min @Load 0.716 lb, Temperature 527 °F	STN EN ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	75.0 MPa	10900 psi	STN EN ISO 527-2
Elongation at Break	2.0 %	2.0 %	STN EN ISO 527-2
Tensile Modulus	3.00 GPa	435 ksi	STN EN ISO 527-2
Flexural Strength	100 MPa	14500 psi	STN EN ISO 178
Flexural Modulus	2.50 GPa	363 ksi	STN EN ISO 178
Charpy Impact Unnotched	7.00 J/cm² @Temperature -20.0 °C	33.3 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179
Charpy Impact, Notched	0.100 J/cm² @Temperature -20.0 °C	0.476 ft-lb/in² @Temperature -4.00 °F	STN EN ISO 179
	0.150 J/cm² @Temperature 23.0 °C	0.714 ft-lb/in² @Temperature 73.4 °F	STN EN ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	STN EN 11357-1

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	80.0 °C @Time 14400 sec	176 °F @Time 4.00 hour
Moisture Content	0.25 %	0.25 %	STN EN ISO 3344
Injection Pressure	70.0 - 120 MPa	10200 - 17400 psi

Descriptive Properties	Value	Comments
Color	Black