Plastcom SLOVALEN PH 99 GB 30 LS PP, 30% glass beads, mod. of mech. properties

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PH 99 GB 30 LS PP, 30% glass beads, mod. of mech. properties.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass beads, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural mode and in the full RAL colour scale.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
Linear Mold Shrinkage 0.0157 cm/cm
0.0157 in/in
Linear Mold Shrinkage, Transverse 0.0168 cm/cm
0.0168 in/in
Melt Flow 5.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
5.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 36.0 MPa
5220 psi
Elongation at Break 8.0 %
8.0 %
Tensile Modulus 3.25 GPa
471 ksi
Flexural Strength 45.0 MPa
6530 psi
Flexural Modulus 3.10 GPa
450 ksi
Charpy Impact Unnotched 3.40 J/cm²

@Temperature -20.0 °C
16.2 ft-lb/in²

@Temperature -4.00 °F
4.10 J/cm²

@Temperature 23.0 °C
19.5 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Vicat Softening Point 101 °C
214 °F
B
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi