Plastcom SLOVAMID® 6 GF 25 E LS PA6 reinforced with glass fiber, UV stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVAMID® 6 GF 25 E LS PA6 reinforced with glass fiber, UV stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6 grade for extrusion, reinforced with 25% glass fiber, determined for extrusion of window profile systems. Delivered in natural as well as full RAL scale color.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 25 % | 25 % | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 275 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 527 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | STN EN ISO 527-2 |
| Elongation at Break | 3.5 % | 3.5 % | STN EN ISO 527-2 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | STN EN ISO 527-2 |
| Flexural Strength | 175 MPa | 25400 psi | STN EN ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 4.40 J/cm² @Temperature -20.0 °C |
20.9 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -20.0 °C |
1.67 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 250 °C | 482 °F | STN EN ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C @Thickness 3.00 mm |
1200 °F @Thickness 0.118 in |
STN EN 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | STN 34 6460 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | STN 34 6460 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | STN EN 60243-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 % | 0.15 % | STN EN ISO 3344 |