Polymer Resources PPX-GP8 Modified PPO, General Purpose, Impact Modified  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Impact Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX-GP8 Modified PPO, General Purpose, Impact Modified  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 8.0 - 14 g/10 min
8.0 - 14 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.8 MPa
6500 psi
ASTM D638
Tensile Strength, Yield 44.8 MPa
6500 psi
ASTM D638
Flexural Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 1.97 GPa
285 ksi
ASTM D790
Izod Impact, Notched 3.74 J/cm
7.00 ft-lb/in
ASTM D256
Gardner Impact >= 36.2 J
>= 26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
240 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ASTM D648
Flammability, UL94 HB
HB
1/16 in
HB
HB
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 243 - 293 °C
470 - 560 °F
Middle Barrel Temperature 254 - 299 °C
490 - 570 °F
Front Barrel Temperature 266 - 304 °C
510 - 580 °F
Melt Temperature 274 - 302 °C
525 - 575 °F
Mold Temperature 65.6 - 98.9 °C
150 - 210 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour