Ravago Manufacturing Americas Hybrid S464 ABS + Polycarbonate Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Ravago Manufacturing Americas, LLC
Trade Name Hybrid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hybrid S464 ABS + Polycarbonate Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
0.125 in; ASTM D955
Melt Flow 3.2 g/10 min

@Load 3.80 kg,
Temperature 230 °C
3.2 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
6.8 g/10 min

@Load 2.16 kg,
Temperature 260 °C
6.8 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
15 g/10 min

@Load 3.80 kg,
Temperature 260 °C
15 g/10 min

@Load 8.38 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 57.2 MPa
8300 psi
ASTM D638
Elongation at Break 70 %
70 %
ASTM D638
Flexural Yield Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 2.34 GPa
340 ksi
ASTM D790
Izod Impact, Notched 6.94 J/cm
13.0 ft-lb/in
73°F, 0.125 in; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 112 °C
234 °F
Unannealed (0.125 in); ASTM D648
Flammability, UL94 HB
HB
0.0590 in
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 243 °C
450 - 470 °F
Middle Barrel Temperature 238 - 249 °C
460 - 480 °F
Front Barrel Temperature 243 - 254 °C
470 - 490 °F
Nozzle Temperature 249 - 260 °C
480 - 500 °F
Mold Temperature 60.0 - 82.2 °C
140 - 180 °F
Drying Temperature 104 °C
220 °F
Dry Time 3 - 4 hour
3 - 4 hour
Moisture Content <= 0.020 %
<= 0.020 %
Injection Pressure 6.89 - 11.7 MPa
1000 - 1700 psi
Shot Size 40 - 80 %
40 - 80 %
Screw Speed 40 - 60 rpm
40 - 60 rpm
Descriptive Properties Value Comments
Injection Rate Moderate