Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Renegade Materials Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures up to 400°F. RM-3002 “next-generation” BMI delivers improved damage tolerance at higher temperatures vs. industry-standard BMI’s. Renegade precision-quality prepregs exhibit excellent handling characteristics and are available in woven and unidirectional form on various fibers including carbon, quartz and S2 glass. A wide variety of nano-materials can be incorporated into this resin system for tailored laminate properties and multi-functional performance. Renegade offers paste (RM-3006 and RM-3007) and film (RM-3011) adhesives compatible with RM-3002. Renegade also offers similar resin systems for RTM (RM-3000) or VARTM (RM-3010) processing.Information provided by Renegade Materials Corporation.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0456 lb/in³
Resin
Mechanical Properties Metric English Comments
Elongation at Break 3.6 %
3.6 %
Resin
Flexural Strength 145 MPa
21000 psi
Resin
Flexural Modulus 4.27 GPa
620 ksi
Resin
Compressive Strength 214 MPa

@Temperature 232 °C
31000 psi

@Temperature 450 °F
Open Hole, Wet; ASTM D7028
262 MPa

@Temperature 204 °C
38000 psi

@Temperature 400 °F
Open Hole, Wet; ASTM D7028
262 MPa

@Temperature 177 °C
38000 psi

@Temperature 350 °F
Open Hole, Wet; ASTM D7028
283 MPa

@Temperature 204 °C
41000 psi

@Temperature 400 °F
Open Hole, Dry; ASTM D7028
303 MPa

@Temperature 177 °C
44000 psi

@Temperature 350 °F
Open Hole, Dry; ASTM D7028
331 MPa

@Temperature 21.1 °C
48000 psi

@Temperature 70.0 °F
Open Hole, Dry; ASTM D7028
Fracture Toughness 0.00213 MPa-m½
0.00194 ksi-in½
Interlaminar, Mode 1, Vf=59.5%; ASTM D5528
0.121 MPa-m½
0.110 ksi-in½
Interlaminar, Mode 2, Vf=59.5%; ASTM D5528
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 232 °C
450 °F
Storage Modulus, Dry, No post cure, Initial cure at 375°F for 3 hrs
235 °C

@Temperature 246 °C,
Time 21600 sec
455 °F

@Temperature 475 °F,
Time 6.00 hour
Storage Modulus, Wet, Vary post cure conditions, cure at 360°F for 6 hrs
248 °C

@Temperature 191 °C,
Time 10800 sec
478 °F

@Temperature 375 °F,
Time 3.00 hour
Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
275 °C

@Temperature 227 °C,
Time 21600 sec
527 °F

@Temperature 440 °F,
Time 6.00 hour
Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
285 °C

@Temperature 246 °C,
Time 21600 sec
545 °F

@Temperature 475 °F,
Time 6.00 hour
Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs
285 °C

@Temperature 227 °C,
Time 21600 sec
545 °F

@Temperature 440 °F,
Time 6.00 hour
Storage Modulus, Dry, Vary post cure conditions, cure at 360°F for 6 hrs
339 °C

@Temperature 266 °C,
Time 21600 sec
642 °F

@Temperature 510 °F,
Time 6.00 hour
Storage Modulus, Dry, Vary post cure conditions, initial cure at 375°F, 3 hrs