SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZFL34 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 91.0 MPa | 13200 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.81 GPa | 988 ksi | 1 mm/min; ISO 527 |
| 7.21 GPa | 1050 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 136 MPa | 19700 psi | ISO 178 | |
| 136 MPa | 19700 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.43 GPa | 933 ksi | 2 mm/min; ISO 178 |
| 6.79 GPa | 985 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.990 J/cm | 1.85 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.16 J/cm | 9.67 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.44 | 0.44 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D3702 Modified |
| K (wear) Factor | 187 x 10-8 mm³/N-M | 93.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.4 µm/m-°C @Temperature -30.0 - 30.0 °C |
34.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 45.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |