SABIC Innovative Plastics LNP LUBRILOY D2000P PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY D2000P PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing, Wear Resistant.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
0.210 %
0.210 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0084 cm/cm

@Time 86400 sec
0.0084 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0081 cm/cm

@Time 86400 sec
0.0081 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ASTM D638
46.0 MPa
6670 psi
ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
ISO 527
56.0 MPa
8120 psi
ASTM D638
Elongation at Break 42.3 %
42.3 %
ASTM D638
43.1 %
43.1 %
ISO 527
Elongation at Yield 5.3 %
5.3 %
ISO 527
5.9 %
5.9 %
ASTM D638
Tensile Modulus 1.93 GPa
280 ksi
50 mm/min; ASTM D638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Strength 86.0 MPa
12500 psi
ASTM D790
86.0 MPa
12500 psi
ISO 178
Flexural Modulus 2.27 GPa
329 ksi
ASTM D790
2.30 GPa
334 ksi
ISO 178
Izod Impact, Notched 4.53 J/cm
8.49 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 40.0 J
29.5 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 43.0 J
31.7 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.19
0.19
ASTM D3702 Modified
Coefficient of Friction, Static 0.15
0.15
ASTM D3702 Modified
K (wear) Factor 88.6 x 10-8 mm³/N-M
44.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
71.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
125 °C

@Thickness 3.20 mm
257 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP