SABIC Innovative Plastics LNP STAT-KON DD000P PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DD000P PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* DD000P is a compound based on Polycarbonate resin containing Carbon. Added features of this material include: Electrically Conductive, Exceptional Processing.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ASTM D792
1.23 g/cc
0.0444 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0074 cm/cm

@Time 86400 sec
0.0074 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
0.0084 cm/cm

@Time 86400 sec
0.0084 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 49.0 MPa
7110 psi
ASTM D638
51.0 MPa
7400 psi
ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
ASTM D638
57.0 MPa
8270 psi
ISO 527
Elongation at Break 9.9 %
9.9 %
ISO 527
20.1 %
20.1 %
ASTM D638
Elongation at Yield 4.8 %
4.8 %
ASTM D638
4.8 %
4.8 %
ISO 527
Tensile Modulus 2.49 GPa
361 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 78.0 MPa
11300 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
2.75 GPa
399 ksi
ASTM D790
Izod Impact, Notched 2.34 J/cm
4.38 ft-lb/in
ASTM D256
Izod Impact, Unnotched 22.26 J/cm
41.70 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 205 kJ/m²
97.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 40.0 J
29.5 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 40.0 J
29.5 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 64.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
64.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
135 °C

@Thickness 3.20 mm
275 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
125 °C

@Thickness 3.20 mm
257 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257