SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing 10% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Flame Retardant.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ASTM D792
1.44 g/cc
0.0520 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
0.130 %
0.130 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 - 0.0080 cm/cm

@Time 86400 sec
0.0070 - 0.0080 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
ASTM D638
126 MPa
18300 psi
ISO 527
Elongation at Break 2.4 %
2.4 %
ISO 527
2.5 %
2.5 %
ASTM D638
Tensile Modulus 8.82 GPa
1280 ksi
50 mm/min; ASTM D638
9.58 GPa
1390 ksi
1 mm/min; ISO 527
Flexural Strength 171 MPa
24800 psi
ASTM D790
185 MPa
26800 psi
ISO 178
Flexural Modulus 5.99 GPa
869 ksi
ASTM D790
7.01 GPa
1020 ksi
ISO 178
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.79 J/cm
7.10 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 9.00 J
6.64 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D3702 Modified
Coefficient of Friction, Static 0.37
0.37
ASTM D3702 Modified
K (wear) Factor 127 x 10-8 mm³/N-M
63.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
18.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
10.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
94.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
164 °C

@Thickness 3.20 mm
327 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Volume Resistivity 1000 ohm-cm - 1e+05
1000 ohm-cm - 1e+05
ASTM D257
Surface Resistance 1000 ohm - 1e+05
1000 ohm - 1e+05
ASTM D257