SABIC Innovative Plastics LNP THERMOCOMP RF00AS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF00AS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF00AS is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 |
| 1.573 g/cc | 0.05683 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.740 % | 0.740 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0034 cm/cm @Time 86400 sec |
0.0034 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0121 cm/cm @Time 86400 sec |
0.0121 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 194 MPa | 28100 psi | ISO 527 |
| 197 MPa | 28600 psi | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min; ISO 527 |
| 17.65 GPa | 2560 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 300 MPa | 43500 psi | ISO 178 |
| 312 MPa | 45300 psi | ASTM D790 | |
| Flexural Modulus | 12.54 GPa | 1819 ksi | ASTM D790 |
| 14.5 GPa | 2100 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.85 J/cm | 29.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 44.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- EG100A Polyurethane-based Biomedical Elastomer
- Heraeus Cleviosâ„¢ P Jet HC V2 Conductive Sulfonate Polymer for Antistatic Coatings
- Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50
- Unifrax Fiberwall® Bonded 30 Bonded Module System
- Polyram PlusTek PA340S8 Nylon 6.6 for Injection Molding, 40% Glass-beads Reinforced
- Chevron Phillips Marlex® HHM 4903 High Density Ethylene Hexene Copolymer
- Braskem TS9022 Blown Film Extrusion Low Density Polyethylene
- ACC QM 230F QSI Quantum Silicones 30 Durometer Addition Cure Moldmaking Material
- Advanced Polymer Alloys DuraGrip™ 6150 BK Melt Processable Elastomer
- DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, General Description (disc