SABIC Innovative Plastics Lexan® EXL4019 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® EXL4019 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers improved ductility over conventional GF reinforced PC resins in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times when compared to standard PC. Lexan EXL4019 resin is a product that may be an excellent candidate for a wide variety of applications.
Available in limited colors only.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D 792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % @Temperature 23.0 °C |
0.15 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 8.7 % | 8.7 % | 5 mm/min; ISO 527 |
| 14 % | 14 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D 638 |
| 4.3 % | 4.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.90 GPa | 566 ksi | 1 mm/min; ISO 527 |
| 3.95 GPa | 573 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| 103 MPa | 14900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.45 GPa | 500 ksi | 2 mm/min; ISO 178 |
| 3.50 GPa | 508 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.50 J/cm @Temperature -30.0 °C |
2.81 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 3.45 J/cm @Temperature 23.0 °C |
6.46 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 146 °C | 295 °F | Rate B/50; ASTM D 1525 |
| 146 °C | 295 °F | Rate B/50; ISO 306 | |
| 146 °C | 295 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S HF 50A-3S1981 Thermoplastic Elastomer (TPE)
- Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Conditioned)
- Momentive Performance Materials FRV1106 Red Fluorosilicone Adhesive Sealant, Fuel Resistant Paste
- Sibur 153-02K 1st Grade Polyethylene for Cable Production
- Struktol TPW 012 Processing Additive
- Tra-Con Tra-Bond 293-1.5T General Purpose Instrument Epoxy Adhesive-Flexible
- Covestro Bayflex® XGT-140 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Asahi Glass AFLAS® 150E TFE/P Fluoroelastomer
- Ineos Nova 5711 High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved