SABIC Innovative Plastics Lexan® FR66 Polycarbonate Film, Flame Retardant

Category Polymer , Film , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FR66 Polycarbonate Film, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan FR66 flame-retardant film is a clear, thin-gauge polycarbonate film with a suede finish on one side and a matte finish on the other, and a UL94 V-0 listing to meet the stringent requirements in a wide range of electrical, electronic and transportation applications. Lexan FR66 film offers ease of thermoforming, hydroforming, embossing, die-cutting, folding and bending and is very suitable for applications such as printed circuit board insulation, backlit aircraft in-flight panels and displays, business equipment insulation, computer rack partitions TV and monitor insulation.Information provided by SABIC Innovative Plastics
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Water Absorption 0.28 %
0.28 %
24 hrs; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 60.0 MPa
8700 psi
ASTM D882
Tensile Strength, Yield 68.9 MPa
9990 psi
ASTM D882
Elongation at Break 100 - 160 %
100 - 160 %
ASTM D882
Tensile Modulus 2.20 GPa
319 ksi
ASTM D882
Gardner Impact 28.5 J

@Thickness 0.762 mm
21.0 ft-lb

@Thickness 0.0300 in
ASTM D3029
Impact Test 12.2 J
9.00 ft-lb
Puncture Resistance, Dynatup; ASTM D3763
Tear Strength 11.6 - 21.2 kN/m
66.2 - 121 pli
propogation; ASTM D1922
245 - 316 kN/m
1400 - 1800 pli
initiation; ASTM D1004
Thermal Properties Metric English Comments
CTE, linear 57.6 µm/m-°C
32.0 µin/in-°F
ASTM E831
Specific Heat Capacity 1.26 J/g-°C

@Temperature 4.00 °C
0.301 BTU/lb-°F

@Temperature 39.2 °F
ASTM E1269
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM D5470
Deflection Temperature at 1.8 MPa (264 psi) 143.3 °C
289.9 °F
TMA
Vicat Softening Point 175 °C
347 °F
ASTM 1525-00 modified
Brittleness Temperature -135 °C
-211 °F
ASTM D746
Glass Transition Temp, Tg 153 °C
307 °F
ASTM D3417/D3418
Flammability, UL94 V-0

@Thickness 0.250 - 0.375 mm
V-0

@Thickness 0.00984 - 0.0148 in
V-0

@Thickness >=0.375 mm
V-0

@Thickness >=0.0148 in
Shrinkage 0.020 %

@Temperature 150 °C
0.020 %

@Temperature 302 °F
ASTM D1204
Optical Properties Metric English Comments
Refractive Index 1.60

@Temperature 25.0 °C
1.60

@Temperature 77.0 °F
ASTM D542A
Gloss 4.0 %
4.0 %
over Flat Black min/max @ 60º; ASTM D523-60
Yellow Index 1.3 %
1.3 %
ASTM D1925
Transmission, Visible 86.1 %
86.1 %
ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Surface Resistivity per Square 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
ASTM D150
2.9

@Frequency 60.0 Hz
2.9

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 59.0 kV/mm

@Temperature 23.0 °C
1500 kV/in

@Temperature 73.4 °F
in oil, short time. 0.25mm; ASTM D149-97a Method A
Dissipation Factor 0.0026

@Frequency 60.0 Hz
0.0026

@Frequency 60.0 Hz
ASTM D150
0.0117

@Frequency 1.00e+6 Hz
0.0117

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 64 sec
64 sec
Tungsten; ASTM D495
Descriptive Properties Value Comments
Fold Endurance (folds) 20
MIT; ASTM D2176-69; double, 0.50mm
60
MIT; ASTM D2176-69; double, 0.25mm
Nominal Gauge Variation (%) 10
0.250mm