- Styron Pulse® A20-95 PC/ABS
Styron Pulse® A20-95 PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® A20-95 PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A medium impact strength PC/ABS blend with high heat distortion and excellent processability.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO R1183 |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | ISO R 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 15 g/10 min @Load 5.00 kg, Temperature 260 °C |
15 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | DIN 53459 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO R 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO R 527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO R 527 |
| Tensile Modulus | 2.05 GPa | 297 ksi | ISO R 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| Izod Impact, Notched | 3.00 J/cm @Temperature -40.0 °C |
5.62 ft-lb/in @Temperature -40.0 °F |
ISO R 180 |
| 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ISO R 180 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
ISO R179 |
| 2.00 J/cm² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
ISO R179 | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO R179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 85.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
44.4 - 47.2 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | unannealed; ISO 75 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | unannealed; ISO 75 A |
| Vicat Softening Point | 109 °C | 228 °F | 50°C/hr, 5 kg; ISO 306 B |
| 127 °C | 261 °F | 120°C/hr, 1 kg; ISO 306 A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 20 % | 20 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers KetaSpire® KT-850 Polyetheretherketone (PEEK) (Unverified Data**)
- Menzolit Menzolit® BMC 0160 Unsaturated Polyester UP
- Ineos L12N-00 Polypropylene Impact Copolymer
- Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F)
- Universal Wire Works Haynes 25 (L-605) (AMS 5796) Filler Metal
- Trelleborg Fillite® 160 Alumino-silicate Cenospheres
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- AK Steel ASTM A 1011, Class 2 Formable, Grade 50K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA)
- Arkema Group KYNAR® 1000 HD Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- AlphaGary Smokeguard™ LS III 1011 Low Smoke Polyvinyl Chloride
Copyright © lookpolymers.com All Rights Reserved