Vyncolit G865 Novolac Phenolic

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit G865 Novolac Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass fiber filled phenolic molding compound with high mechanical, good thermal and electrical properties. USES: Asbestos-free replacement for die-cast automotive metal parts, e.g. reactors for automatic gear boxes. Multi-V pulleys.Information provided by Vyncolit, a Sumitomo Bakelite Group
Physical Properties Metric English Comments
Bulk Density 0.700 g/cc
0.0253 lb/in³
Powder Density; ISO 60
Density 1.85 g/cc
0.0668 lb/in³
Relative Density; ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
Injection Molding; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
ISO 527
Elongation at Break 0.50 %
0.50 %
Tensile; ISO 527
1.0 %
1.0 %
Flexure; ISO 178
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527
Flexural Strength 150 MPa
21800 psi
At Rupture; ISO 178
Flexural Modulus 16.0 GPa
2320 ksi
ISO 178
Compressive Strength 190 MPa
27600 psi
ISO 604
Charpy Impact Unnotched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 20.0 °C
13.9 µin/in-°F

@Temperature 68.0 °F
TMA
CTE, linear, Transverse to Flow 30.0 µm/m-°C

@Temperature 20.0 °C
16.7 µin/in-°F

@Temperature 68.0 °F
TMA
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75 Af
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 4.00 mm
V-0

@Thickness 0.157 in
Shrinkage 0.10 %
0.10 %
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 243
Comparative Tracking Index 175 V
175 V
IEC 112
Descriptive Properties Value Comments
Color Black
ISO type PF 2 C3
Main Filler Glass Fiber
Molding Method Compression, transfer, injection