BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 Q611 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 6.6 % | 6.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 130 cm³/g | 130 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 275 °C |
25 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1mm/min; ISO 527 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359 |
| Melting Point | 220 °C | 428 °F | 10 K/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP2 PC (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 1105-7766 PEEK, with carbon fiber, easy flowing
- Lanxess Durethan® BKV 115 H3.0 000000 Nylon 6-Copolymer, Glass Fiber Reinforced
- SABIC Innovative Plastics LNP STAT-KON DEF42 PC (Asia Pacific)
- Süd-Chemie Nanofil® 2 Polymer Additive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.5 PHR Sulfur
- Dow DOWLEX™ 2071 Linear Low Density Polyethylene
- DuPont Teijin Films Melinex® 623 Polyester Film, 1000 Gauge
- Colorite Polymers Vinylbond 95-950-60 PVC Compound
- Alliance Polymers Viprene™ G85A-32U-NAT Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved