DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and modulus than Delrin® 100P.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 Immersion 24h; ASTM D570
1.0 %

@Temperature 23.0 °C
 1.0 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage 0.017 - 0.020 cm/cm

@Thickness 3.20 mm
 0.017 - 0.020 in/in

@Thickness 0.126 in
 Transverse, 24h; ASTM D955
0.018 - 0.021 cm/cm

@Thickness 3.20 mm
 0.018 - 0.021 in/in

@Thickness 0.126 in
 Flow, 24h; ASTM D955
Linear Mold Shrinkage, Flow 0.018 - 0.021 cm/cm

@Thickness 4.00 mm
 0.018 - 0.021 in/in

@Thickness 0.157 in
 Parallel, 24h; ISO 294-4
0.021 cm/cm

@Thickness 2.00 mm
 0.021 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Thickness 2.00 mm
 0.019 in/in

@Thickness 0.0787 in
 ISO 294-4
0.018 - 0.021 cm/cm

@Thickness 4.00 mm
 0.018 - 0.021 in/in

@Thickness 0.157 in
 Normal, 24h; ISO 294-4
Melt Flow 1.0 g/10 min

@Load 1.05 kg,
Temperature 190 °C
 1.0 g/10 min

@Load 2.31 lb,
Temperature 374 °F
 ASTM D1238
2.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 2.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Melt Index of Compound 1.9 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 1.9 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039/2
Hardness, Rockwell R 120
120
ISO 2039/2
121
121
ASTM D785
Tensile Strength 72.0 MPa

@Temperature 23.0 °C
 10400 psi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Tensile Stress 60.799 MPa

@Strain 2.8574 %,
Temperature -40.0 °C
 8818.2 psi

@Strain 2.8574 %,
Temperature -40.0 °F
 ISO 527
87.176 MPa

@Strain 5.7149 %,
Temperature -40.0 °C
 12644 psi

@Strain 5.7149 %,
Temperature -40.0 °F
 ISO 527
94.877 MPa

@Strain 8.5723 %,
Temperature -40.0 °C
 13761 psi

@Strain 8.5723 %,
Temperature -40.0 °F
 ISO 527
96.84 MPa

@Strain 11.43 %,
Temperature -40.0 °C
 14050 psi

@Strain 11.43 %,
Temperature -40.0 °F
 ISO 527
97.432 MPa

@Strain 14.287 %,
Temperature -40.0 °C
 14131 psi

@Strain 14.287 %,
Temperature -40.0 °F
 ISO 527
97.672 MPa

@Strain 17.145 %,
Temperature -40.0 °C
 14166 psi

@Strain 17.145 %,
Temperature -40.0 °F
 ISO 527
98.055 MPa

@Strain 20.002 %,
Temperature -40.0 °C
 14222 psi

@Strain 20.002 %,
Temperature -40.0 °F
 ISO 527
98.733 MPa

@Strain 22.86 %,
Temperature -40.0 °C
 14320 psi

@Strain 22.86 %,
Temperature -40.0 °F
 ISO 527
99.053 MPa

@Strain 25.717 %,
Temperature -40.0 °C
 14366 psi

@Strain 25.717 %,
Temperature -40.0 °F
 ISO 527
99.549 MPa

@Strain 28.574 %,
Temperature -40.0 °C
 14438 psi

@Strain 28.574 %,
Temperature -40.0 °F
 ISO 527
Tensile Strength, Yield 72.0 MPa

@Temperature 23.0 °C
 10400 psi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
72.0 MPa

@Temperature 23.0 °C
 10400 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 40 %

@Temperature 23.0 °C
 40 %

@Temperature 73.4 °F
 nominal; ISO 527
50 %

@Temperature 23.0 °C
 50 %

@Temperature 73.4 °F
 ISO 527
73 %

@Temperature 23.0 °C
 73 %

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Elongation at Yield 20 %

@Temperature 23.0 °C
 20 %

@Temperature 73.4 °F
 ISO 527
21 %

@Temperature 23.0 °C
 21 %

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
Tensile Modulus 3.00 GPa

@Temperature 23.0 °C
 435 ksi

@Temperature 73.4 °F
 5mm/min (0.2in/min); ASTM D638
3.20 GPa

@Temperature 23.0 °C
 464 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 80.0 MPa

@Strain 3.50 %,
Temperature 23.0 °C
 11600 psi

@Strain 3.50 %,
Temperature 73.4 °F
 ISO 178
92.0 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 13300 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ASTM D790
Flexural Modulus 2.90 GPa

@Temperature 23.0 °C
 421 ksi

@Temperature 73.4 °F
 ISO 178
2.97 GPa

@Temperature 23.0 °C
 431 ksi

@Temperature 73.4 °F
 ASTM D790
Izod Impact, Notched 0.960 J/cm

@Temperature 23.0 °C
 1.80 ft-lb/in

@Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
11.0 kJ/m²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched 27.0 J/cm²

@Temperature -30.0 °C
 128 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
30.0 J/cm²

@Temperature 23.0 °C
 143 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.10 J/cm²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 3000 MPa

@Temperature 23.0 °C
 435000 psi

@Temperature 73.4 °F
 ISO 899
Tensile Creep Modulus, 1000 hours 1700 MPa

@Temperature 23.0 °C
 247000 psi

@Temperature 73.4 °F
 ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 100 °C
 278 µin/in-°F

@Temperature 131 - 212 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 94.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 52.2 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
110 µm/m-°C

@Temperature 23.0 - 55.0 °C
 61.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ASTM E 831
110 µm/m-°C

@Temperature 23.0 - 55.0 °C
 61.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+14 ohm-cm

@Temperature 23.0 °C
 8.00e+14 ohm-cm

@Temperature 73.4 °F
 ASTM D257
Surface Resistance 6.00e+14 ohm

@Temperature 23.0 °C
 6.00e+14 ohm

@Temperature 73.4 °F
 ASTM D257
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 3.7

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 ASTM D150
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm,
Temperature 23.0 °C
 457 kV/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Short Time; ASTM D149
Dissipation Factor 0.0050

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 0.0050

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 ASTM D150
Comparative Tracking Index 600 V

@Temperature 23.0 °C
 600 V

@Temperature 73.4 °F
 IEC 60112
600 V

@Thickness 3.00 mm,
Temperature 23.0 °C
 600 V

@Thickness 0.118 in,
Temperature 73.4 °F
 UL 746A