DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/Nylon 6 Blend, Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
33% Glass Reinforced UV Stabilized Polyamide 66 + Polyamide 6 Zytel 74G33W BK196 is a high gloss automotive weatherable black 33% glass reinforced nylon 66 and nylon 6 comelt resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
50%RH; ISO 527-1/-2
185 MPa
26800 psi
DAM; ISO 527-1/-2
Tensile Stress 17.25 MPa

@Strain 0.500 %,
Temperature 150 °C
2502 psi

@Strain 0.500 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
19.81 MPa

@Strain 0.500 %,
Temperature 150 °C
2873 psi

@Strain 0.500 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
25.04 MPa

@Strain 0.800 %,
Temperature 150 °C
3632 psi

@Strain 0.800 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
29.4 MPa

@Strain 0.800 %,
Temperature 150 °C
4260 psi

@Strain 0.800 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
34.32 MPa

@Strain 0.500 %,
Temperature 23.0 °C
4978 psi

@Strain 0.500 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
47.63 MPa

@Strain 0.500 %,
Temperature 0.000 °C
6908 psi

@Strain 0.500 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
51.03 MPa

@Strain 0.800 %,
Temperature 23.0 °C
7401 psi

@Strain 0.800 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
51.79 MPa

@Strain 0.500 %,
Temperature 23.0 °C
7512 psi

@Strain 0.500 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
52.32 MPa

@Strain 3.00 %,
Temperature 150 °C
7588 psi

@Strain 3.00 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
52.51 MPa

@Strain 0.500 %,
Temperature 0.000 °C
7616 psi

@Strain 0.500 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
62.37 MPa

@Strain 3.00 %,
Temperature 150 °C
9046 psi

@Strain 3.00 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
68.8 MPa

@Strain 7.00 %,
Temperature 150 °C
9980 psi

@Strain 7.00 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
69.0 MPa

@Strain 0.600 %,
Temperature -40.0 °C
10000 psi

@Strain 0.600 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
73.62 MPa

@Strain 0.800 %,
Temperature 0.000 °C
10680 psi

@Strain 0.800 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
81.37 MPa

@Strain 7.00 %,
Temperature 150 °C
11800 psi

@Strain 7.00 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
88.69 MPa

@Strain 0.900 %,
Temperature 23.0 °C
12860 psi

@Strain 0.900 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
94.24 MPa

@Strain 2.00 %,
Temperature 23.0 °C
13670 psi

@Strain 2.00 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
99.51 MPa

@Strain 1.00 %,
Temperature -40.0 °C
14430 psi

@Strain 1.00 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
99.72 MPa

@Strain 0.900 %,
Temperature -40.0 °C
14460 psi

@Strain 0.900 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
101.04 MPa

@Strain 1.00 %,
Temperature 0.000 °C
14655 psi

@Strain 1.00 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
127 MPa

@Strain 1.30 %,
Temperature 0.000 °C
18400 psi

@Strain 1.30 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
127.87 MPa

@Strain 1.30 %,
Temperature -40.0 °C
18546 psi

@Strain 1.30 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
131.52 MPa

@Strain 5.00 %,
Temperature 23.0 °C
19075 psi

@Strain 5.00 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
139.05 MPa

@Strain 2.00 %,
Temperature 0.000 °C
20168 psi

@Strain 2.00 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
154.06 MPa

@Strain 1.60 %,
Temperature -40.0 °C
22345 psi

@Strain 1.60 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
165.68 MPa

@Strain 2.10 %,
Temperature 23.0 °C
24030 psi

@Strain 2.10 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
170.75 MPa

@Strain 3.20 %,
Temperature 0.000 °C
24765 psi

@Strain 3.20 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
198.51 MPa

@Strain 2.50 %,
Temperature 0.000 °C
28791 psi

@Strain 2.50 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
227.78 MPa

@Strain 3.00 %,
Temperature -40.0 °C
33037 psi

@Strain 3.00 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
DAM; ISO 527-1/-2
6.0 %
6.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 7.08 GPa
1030 ksi
50%RH; ISO 527-1/-2
10.0 GPa
1450 ksi
DAM; ISO 527-1/-2
Flexural Modulus 8.90 GPa
1290 ksi
DAM; ISO 178
Secant Modulus 1.18 GPa

@Strain 9.00 %,
Temperature 100 °C
171 ksi

@Strain 9.00 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
1.20 GPa

@Strain 7.00 %,
Temperature 100 °C
174 ksi

@Strain 7.00 %,
Temperature 212 °F
50%RH; ISO 11403-1 -2
2.2685 GPa

@Strain 4.00 %,
Temperature 100 °C
329.02 ksi

@Strain 4.00 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
2.735 GPa

@Strain 2.00 %,
Temperature 100 °C
396.7 ksi

@Strain 2.00 %,
Temperature 212 °F
50%RH; ISO 11403-1 -2
3.878 GPa

@Strain 3.00 %,
Temperature 23.0 °C
562.5 ksi

@Strain 3.00 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
3.91 GPa

@Strain 0.700 %,
Temperature 100 °C
566 ksi

@Strain 0.700 %,
Temperature 212 °F
50%RH; ISO 11403-1 -2
4.25 GPa

@Strain 0.400 %,
Temperature 100 °C
616 ksi

@Strain 0.400 %,
Temperature 212 °F
50%RH; ISO 11403-1 -2
4.36 GPa

@Strain 0.900 %,
Temperature 100 °C
632 ksi

@Strain 0.900 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
4.884 GPa

@Strain 0.500 %,
Temperature 100 °C
708.4 ksi

@Strain 0.500 %,
Temperature 212 °F
DAM; ISO 11403-1 -2
5.12 GPa

@Strain 3.40 %,
Temperature 0.000 °C
743 ksi

@Strain 3.40 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
5.581 GPa

@Strain 3.00 %,
Temperature 0.000 °C
809.5 ksi

@Strain 3.00 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
6.25 GPa

@Strain 3.10 %,
Temperature 23.0 °C
906 ksi

@Strain 3.10 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
6.38 GPa

@Strain 0.800 %,
Temperature 23.0 °C
925 ksi

@Strain 0.800 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
6.864 GPa

@Strain 0.500 %,
Temperature 23.0 °C
995.6 ksi

@Strain 0.500 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
7.09 GPa

@Strain 3.40 %,
Temperature -40.0 °C
1030 ksi

@Strain 3.40 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2
8.63 GPa

@Strain 2.60 %,
Temperature -40.0 °C
1250 ksi

@Strain 2.60 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
9.2025 GPa

@Strain 0.800 %,
Temperature 0.000 °C
1334.7 ksi

@Strain 0.800 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
9.526 GPa

@Strain 0.500 %,
Temperature 0.000 °C
1382 ksi

@Strain 0.500 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
9.64 GPa

@Strain 1.40 %,
Temperature 0.000 °C
1400 ksi

@Strain 1.40 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
9.84 GPa

@Strain 1.30 %,
Temperature -40.0 °C
1430 ksi

@Strain 1.30 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
9.85 GPa

@Strain 0.900 %,
Temperature 23.0 °C
1430 ksi

@Strain 0.900 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
9.951 GPa

@Strain 1.00 %,
Temperature -40.0 °C
1443 ksi

@Strain 1.00 %,
Temperature -40.0 °F
DAM; ISO 11403-1 -2
10.104 GPa

@Strain 1.00 %,
Temperature 0.000 °C
1465.5 ksi

@Strain 1.00 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
10.358 GPa

@Strain 0.500 %,
Temperature 23.0 °C
1502.3 ksi

@Strain 0.500 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
10.502 GPa

@Strain 0.500 %,
Temperature 0.000 °C
1523.2 ksi

@Strain 0.500 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
11.08 GPa

@Strain 0.900 %,
Temperature -40.0 °C
1607 ksi

@Strain 0.900 %,
Temperature -40.0 °F
50%RH; ISO 11403-1 -2