- DuPont Performance Polymers Zytel® HTN 53G50HSLR BK083 Polyphthalamide (PPA) (Unverified Data**)
DuPont Performance Polymers Zytel® HTN 53G50HSLR BK083 Polyphthalamide (PPA) (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® HTN 53G50HSLR BK083 Polyphthalamide (PPA)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® HTN53G50HSLR BK083 is a 50% glass reinforced, heat stabilized, lubricated high performance polyamide resin developed for moderate temperature structural applications requiring retention of high impact and stiffness.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | DAM; ISO 1183 |
| Filler Content | 50 % | 50 % | DAM |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm |
0.0020 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 215 MPa @Temperature 23.0 °C |
31200 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 250 MPa @Temperature 23.0 °C |
36300 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 2.7 % @Temperature 23.0 °C |
2.7 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 16.5 GPa @Temperature 23.0 °C |
2390 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 16.5 GPa @Temperature 23.0 °C |
2390 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Flexural Modulus | 15.3 GPa @Temperature 23.0 °C |
2220 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
| Izod Impact, Notched (ISO) | 13.5 kJ/m² @Temperature -40.0 °C |
6.42 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
| 14.5 kJ/m² @Temperature 23.0 °C |
6.90 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1U |
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| 9.50 J/cm² @Temperature -40.0 °C |
45.2 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA | |
| 1.40 J/cm² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA | |
| 1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |
| 1.60 J/cm² @Temperature -40.0 °C |
7.61 ft-lb/in² @Temperature -40.0 °F |
50%RH; ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 7500 MPa @Temperature 23.0 °C |
1.09e+6 psi @Temperature 73.4 °F |
50%RH; ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
| 500 µm/m-°C @Temperature 125 - 160 °C |
278 µin/in-°F @Temperature 257 - 320 °F |
DAM; ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 59.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
32.8 µin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 |
| 59.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
32.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| 95.0 µm/m-°C @Temperature 55.0 - 160 °C |
52.8 µin/in-°F @Temperature 131 - 320 °F |
DAM; ISO 11359-1/-2 | |
| Melting Point | 260 °C | 500 °F | 10°C/min, First Heat; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | DAM; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; IEC 60695-11-10 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
DAM; UL94 | |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
DAM; UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
DAM; UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V @Temperature 23.0 °C |
550 V @Temperature 73.4 °F |
DAM; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 95.0 °C | 203 °F | DAM; optimum |
| 85.0 - 105 °C | 185 - 221 °F | DAM | |
| Drying Temperature | 100 °C | 212 °F | DAM |
| Dry Time | 6.00 - 8.00 hour | 6.00 - 8.00 hour | DAM |
| Moisture Content | <= 0.10 % | <= 0.10 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black Color | DAM |
| Filler | Glass Fiber reinforcement | DAM |
| Forms | Pellets | DAM |
| Generic | Polyamide, High Performance (HPPA) | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA-GF50< | ISO 11469; DAM |
| >PA-GF50< | SAE J1344; DAM | |
| Polymer Family | High performance polyamide | DAM |
| Polymer Type | Partially Aromatic PA | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass Reinforced Resins | DAM |
| Superstructural Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA-GF50 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
Users viewing this material also viewed the following:
- Okulen® 2000 PE-UHMW, GB
- LNP Stat-Kon® LCL-4026 EM BK8-115 Polyetheretherketone, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant (d
- Huntsman PE1356 EVA Film Extrusion (discontinued **)
- Ipiranga Petrochem PH 0141 Polypropylene
- Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone
- Plenco 7507 Phenolic, Granular, Transfer Molded
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- Loctite® 3107 Acrylic Light Cure Adhesive
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 15 Minutes Milling
- Dow UNIVAL™ DMDA-6320 NT 7 High Density Polyethylene Resin (HDPE)
Copyright © lookpolymers.com All Rights Reserved