Processing Properties	Metric	English	Comments
Melt Temperature	280 - 300 °C	536 - 572 °F
Plastcom SLOVAMID 66 FRC 2 PA66, basic type FeaturesModified for general use, with excellent manufacturing properties, characterized by high strength and toughness also at minus temperatures. Used in automotive, electrical, engineering and co..
Melt Temperature	280 - 300 °C	536 - 572 °F
Plastcom SLOVAMID 66 GF 10 FRA 3 PA66, 10% glass fibre Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0..
Melt Temperature	280 - 300 °C	536 - 572 °F
Plastcom SLOVAMID 66 GF 30 HI PA66, 30% glass fibre, improved strength FeaturesPA 66 for injection moulding, chemically strengthened with 30% glass fibre and with the content of thermoplastic kaoutchouc. Application: impacted mouldings and mouldings with high strength ..
Melt Temperature	280 - 320 Â°C	536 - 608 Â°F
LG Chemical LUCON CP-4201F Conductive Thermoplastic, Flame Retardant LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..
Melt Temperature	280 - 300 Â°C	536 - 572 Â°F	Injection Molding
LG Chemical LUCON PO6063 mPPO+CNT+CF+GF Description: Injection Molding, mPPO+CNT+CF+GF, Electrostatic Dissipation, High Strength, Low WarpageApplication: LCD Cell TrayCAS No. 35134-01-4, 65997-17-3, 7440-44-0 and 7782-42-5Information prov..
Melt Temperature	280 - 300 Â°C	536 - 572 Â°F	ISO 294
Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Conditioned) Information provided by Gromax Enterprises Corp.
Melt Temperature	280 - 300 Â°C	536 - 572 Â°F	Recommended
Lanxess DurethanÂ® AKV 15 H3.0 000000 Nylon 66, 15% Glass Fibers PA 66, 15% glass fibers, injection molding, heat-ageing stabilized
Melt Temperature	280 - 300 Â°C	536 - 572 Â°F
Lanxess DurethanÂ® AKV 30 000000 Nylon 66, Glass Fiber Reinforced PA 66, 30% glass fibers, injection moldingInformation provided by LANXESS.
Melt Temperature	280 Â°C	536 Â°F	for test specimens; ISO 294
Lanxess DurethanÂ® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Melt Temperature	280 - 300 Â°C	536 - 572 Â°F
LATI Latigray 66-01 CX/50 PA 66 Radiopaque compound based on Polyamide 66 (PA66). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria..
Melt Temperature	280 Â°C	536 Â°F
Solvay Specialty Polymers IxefÂ® FC-1022 Polyarylamide (PARA), 50% Glass Fiber (Conditioned) IxefÂ® FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.Feat..
Melt Temperature	280 - 300 °C	536 - 572 °F
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Melt Temperature	280 - 305 °C	536 - 581 °F
A. Schulman SCHULAMID® 66 MV3 Unreinforced Nylon 6/6 Information provided by A. Schulman.
Melt Temperature	280 - 305 °C	536 - 581 °F
A. Schulman SCHULAMID® 66 MV3 Unreinforced Nylon 6/6 Information provided by A. Schulman.
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® 2558 Polycarbonate ISO 7391-PC,MR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minMedical devicessuitable for ETO and steam sterilization at 121 °CComplies with the requirements of FDA-modified ISO 10993-1 and USP Class..
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® 3156 Polycarbonate ISO 7391-PC,MR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFood contact qualityHigh viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtru..
Melt Temperature	280 °C	536 °F	Injection Molding; ISO 294
Covestro Makrolon® 6267 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFLR,(,,)-18-9Formerly Makrolon DP1-1872MVR (300 °C/1.2 kg) 19 cm3/10 minFlame retardantUL 94V-0/1.5 mmLow viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 3..
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® 6357 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFLR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-0/3.0 mmMedium viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 2..
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® 6457 Polycarbonate, Flame Retardant Grade MVR (300 °C/1.2 kg) 12.5 cm3/10 minUL 94V-0/3.0 mmUV stabilizedeasy releaseinjection moldingavailable in transparent, translucent and opaque colorsPreprocessingMax. Water content
Melt Temperature	280 °C	536 °F	Injection Molding; ISO 294
Covestro Makrolon® AL2447 Polycarbonate ISO 7391-PC,MLR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 19 cm3/10 minAutomotive lightingLow viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transpa..
Melt Temperature	280 - 300 °C	536 - 572 °F	DAM
DuPont Performance Polymers Zytel® FE3071 NC010 Nylon 66 Zytel® FE3071 NC010 is an intermediate viscosity polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Melt Temperature	280 - 305 °C	536 - 581 °F
E-Polymers TEKAMID® JN110 PPE+PA66 Filler Reinforced PA/PPE Alloy Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/P..
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® 1248 Polycarbonate, Impact Grade ISO 7391-PC,MP,(,,)-09-9Formerly Makrolon KU1-1248MVR (300 °C/1.2 kg) 7.0 cm3/10 minFood contact qualityMedium viscosityImpact modifiedInjection molding - Melt temperature 280 - 320 °CAvailable in..
Melt Temperature	280 - 320 °C	536 - 608 °F
Covestro Makrolon® DP1-1843* Polycarbonate ISO 7391-PC,RL,(,,)-09-9Developmental productMVR (300 °C/1.2 kg) 9.5 cm3/10 minMedium viscosityUV stabilizedRotomoldingAvailable in transparent and translucent colorsGlobe lightsAs of 1 September 2..
Melt Temperature	280 °C	536 °F	Injection molding
BASF Ultramid® 8350 HS BK-102 PA6 (Conditioned) Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a..
Melt Temperature	280 °C	536 °F	Injection molding
BASF Ultramid® 8350 HS PA6 (Conditioned) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate..
Melt Temperature	280 - 300 °C	536 - 572 °F
E-Polymers SEPAZ® LA50 PA66 LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver..
Melt Temperature	280 - 310 °C	536 - 590 °F
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS) (discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..
Melt Temperature	280 °C	536 °F	Optimal
BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Dry) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade used e.g. for automobile manifold.Information provided by BASF
Melt Temperature	280 °C	536 °F	Injection molding; ISO 294
Lanxess Durethan® AKV 25 F30 000000 Nylon 66, 25% Glass Fiber PA 66, 25% glass fiber, injection molding, flame retardantInformation provided by LANXESS.