Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA6 30V D51 PA6, Glass Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA6 30V D51 is a PTFE Lubricated, Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 156 MPa | 22600 psi | ISO 527 |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 |
| Flexural Strength | 215 MPa | 31200 psi | ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 20-0665 Polyphthalamide, with carbon fiber, PTFE, lubricant modified
- Iran Petrochemical (PCC) EX 5 HM 9450 F High Density Polyethylene
- SABIC Innovative Plastics NORYL SE1V PPE+HIPS (Asia Pacific)
- SGL Carbon Group SIGRAFIL C® in 250°F Epoxy
- Solvay Specialty Polymers Tecnoflon® VPL 85540 / VPL 55540 Fluoroelastomer
- SABIC Innovative Plastics NORYL NH4030B PPE+HIPS
- Tipco Tipcolene® CR 8233 - 20% Talc/Mineral Reinforced Polypropylene Copolymer Compound
- A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy
- EMS-Grivory Grivory® LVX-50H black 9230 PA12-GF50
- Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing
Copyright © lookpolymers.com All Rights Reserved