Ineos Nova 4214 Medium Impact Polystyrene (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova 4214 Medium Impact Polystyrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | Condition G |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 57 | 57 | |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Modulus of Elasticity | 2.759 GPa | 400.2 ksi | ASTM D638 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.759 GPa | 400.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm @Diameter 3.17 mm |
1.59 ft-lb/in @Diameter 0.125 in |
bar, 0.010" notch radius; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.59 @Frequency 1e+6 Hz |
2.59 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 19.7 kV/mm @Thickness 3.17 mm |
500 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML3290 PC (Europe-Africa-Middle East)
- LyondellBasell Alathon® H5642 High Density Polyethylene, Injection Molding Grade (discontinued **)
- Kolon ELLAS K-470A Ester Based Thermoplastic Polyurethane
- Solvay Chemicals 4_Ethoxy_1_1_1_trifluoro_3_buten_2_one
- Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant
- SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film
- Eastman Tritan TX1800 Copolyester
- ExxonMobil Exxtral™ LNT 010 Performance Polyolefin
- CMW® ELKONITE® 40S Infiltrated Tungsten Silver contact material ASTM B631
Copyright © lookpolymers.com All Rights Reserved