LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 20% Glass Fiber Reinforced
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)  (discontinued **).pdf
  Online Service   lookpolymers   27660005
Material Notes:
Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gears, cams, bushings, and other parts for the electromechanical, hydraulic, and automotive sectors, and others). A good resistance to hydrolysis makes it usable in hot water up to 80°-90°C. Basic Latan versions featuring low or high flowability are available, as well as an elastomer modified version to improve product toughness.Specific Notes for this Material: 15% glass fiber; good mechanical properties. Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.20 %
0.20 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
Linear Mold Shrinkage, Transverse 0.0135 cm/cm
0.0135 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 84
Tensile Strength, Ultimate 73.0 MPa
10600 psi
ISO 527
32.0 MPa

@Temperature 120 °C
4640 psi

@Temperature 248 °F
ISO 527
43.0 MPa

@Temperature 90.0 °C
6240 psi

@Temperature 194 °F
ISO 527
50.0 MPa

@Temperature 60.0 °C
7250 psi

@Temperature 140 °F
ISO 527
Flexural Modulus 5.10 GPa
740 ksi
2.40 GPa

@Temperature 120 °C
348 ksi

@Temperature 248 °F
3.10 GPa

@Temperature 90.0 °C
450 ksi

@Temperature 194 °F
3.90 GPa

@Temperature 60.0 °C
566 ksi

@Temperature 140 °F
Izod Impact, Notched 0.600 J/cm

@Temperature 23.0 °C
1.12 ft-lb/in

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point 158 °C
316 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm

@Thickness 0.0591 in
Oxygen Index 18 %
18 %
ISO 4589
Electrical Properties Metric English Comments
Dielectric Strength 22.0 kV/mm

@Thickness 2.00 mm
559 kV/in

@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index >= 600 V
>= 600 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Not essential, temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Not essential, drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) Y
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed medium
Needle Burner Test N
1.47 mm
3.05 mm