- Lavergne VYPET VNT 325 PET 25% Glass - Mineral Reinforced
Lavergne VYPET VNT 325 PET 25% Glass - Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced |
| Manufacturer | Lavergne Performance Compounds |
| Trade Name | VYPET |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lavergne VYPET VNT 325 PET 25% Glass - Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Vypet 325 is a 25% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications.Features: High temperature performance; Good balance resilience-stiffness; Low warpageTypical Applications: Electric parts; Brackets/Connectors; Heat resistant handlesInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
ASTM D955 |
| Ash | 25 % | 25 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | |
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IS7015 Unitape Unidirectional Polypropylene-Glass Composite
- DSM Akulon® K224-HG5 (Cond.) 25% Glass Reinforced Nylon 6 (North America) (discontinued **)
- ICO Polymers ICORENEâ„¢ 195-4060 LMDPE Rotational Molding Resin
- Heatbath/Park Scale Kleen 5 Descaling Salt
- SABIC Innovative Plastics LNP THERMOCOMP PF00ASXS PA 6
- Dow Corning SYL-OFF® PMCP7671 Coating
- Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- C.O.I.M. LARIPUR® LPR5760 PTMG Polyether Polyurethane
- BASF Elastollan S 64 D TPUR
Copyright © lookpolymers.com All Rights Reserved