Menzolit Menzolit® MMC 1600 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® MMC 1600 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MMC 1600 is a mineral moulding compound (similar to DMC/BMC) providing of a stone like appearance eg. granite or marble. Chrome plated mould surfaces are required. It is recommended that product thickness is not less than 3mm.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0016 cm/cm | 0.0016 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 12.0 MPa @Temperature 22.0 °C |
1740 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 12.0 MPa @Temperature 22.0 °C |
1740 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Modulus of Elasticity | 6.00 GPa | 870 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 30.0 MPa @Temperature 22.0 °C |
4350 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 6.00 GPa @Temperature 22.0 °C |
870 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 2.30 GPa | 334 ksi | in plane |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Oxygen Index | 35 % | 35 % | ISO 4589-2 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 145 - 165 °C | 293 - 329 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- Oceanchem Group ANTIOXIDANT SK-900
- Mitsubishi Hostaphan® RN, 350 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific)
- Spartech Royalstatâ„¢ R671 ABS Static Control Sheet
- Unifrax Fiberfrax® HS70 High Purity High-Index Fiber
- A. Schulman LP551-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- CMW® ELKON 100W Pure Tungsten
- Aclo Accutech Polypropylene CP0437T40V Copolymer Talc Reinforced
- Eurofoam Porocell 251 GR NBR/PVC Foam
- Resinlab® EP1190 Flame Retardant Epoxy Casting Resin
Copyright © lookpolymers.com All Rights Reserved