PolyOne Bergamid™ B70 VN4805 LS PM-Z BK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ B70 VN4805 LS PM-Z BK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc @Temperature 23.0 °C |
0.0387 lb/in³ @Temperature 73.4 °F |
±0.02; ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
8990 psi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/50 |
| Elongation at Break | >= 30 % @Thickness 4.00 mm, Temperature 23.0 °C |
>= 30 % @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/50 |
| Elongation at Yield | 4.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
4.0 % @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2/50 |
| Tensile Modulus | 2.60 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
377 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/50 |
| Flexural Strength | 63.0 MPa @Temperature 23.0 °C |
9140 psi @Temperature 73.4 °F |
Injection Molded; ISO 178 |
| Flexural Modulus | 2.00 GPa @Temperature 23.0 °C |
290 ksi @Temperature 73.4 °F |
Injection Molded; ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Injection Molded; ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Injection Molded; ISO 179 |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ALL; UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 60.0 °C | 140 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Impact Modified | |
| Laser Markable | ||
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY CR8510 ASA (Asia Pacific)
- Polymer Resources PC-FR3A-D Polycarbonate, Flame Retardant, High Flow
- Rogers Corporation Bisco® MF1 6535 - 35 Silicone, High Performance Foam, Indentation Force Material
- LG Chemical Lupoy 1201-08 Polycarbonate Resin
- SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA 6/12 (Asia Pacific)
- Wellman EcoLon® MRGF1882-BK1(GPE) Nylon 66, 40% Mineral and Glass Reinforced
- Wieland 1911 Wilaform Gold
- Covestro Makrolon® SF800Z Polycarbonate, 5% Glass Filled
- Polyram PlusTek RA320G3 Nylon 6.6, 15% Glass Fiber, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved