Polykemi AB POLYshine PBT D223 GF30 FR PBT, Glass-Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Polykemi AB
Trade Name POLYshine
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYshine PBT D223 GF30 FR PBT, Glass-Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.012 cm/cm
0.012 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 135 MPa
<= 19600 psi
ISO/R527
Elongation at Break 2.3 %
2.3 %
ISO/R527
Flexural Strength <= 175 MPa
<= 25400 psi
ISO 178
Flexural Modulus 8.00 GPa

@Temperature 23.0 °C
 1160 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
0.600 J/cm²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
120°C/h; ISO 75/1
Vicat Softening Point 210 °C

@Load 5.001 kg
 410 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 IEC 695-2-1