| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Premix Thermoplastics PRE-ELEC® TPE 1501 Conductive Thermoplastic Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PRE-ELEC® TPE 1501 is a conductive thermoplastic compound based on a thermoplastic elastomer (TPE). Conductivity is achieved by using a special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPE 1501 has retained the excellent mechanical properties of the base elastomer.Applications: Extruded profiles, sheets and injection moulded technical parts.Processing: PRE-ELEC® TPE 1501 compound can be extruded or injection moulded in the machines using normal processing conditions as with TPE.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Thickness | 102 microns | 4.00 mil | |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | ISO 294-4 |
| Melt Flow | 11 g/10 min @Load 10.0 kg, Temperature 190 °C |
11 g/10 min @Load 22.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ISO 868 |
| Tensile Strength | 6.70 MPa | 972 psi | ISO 527 |
| Tensile Strength, Yield | 6.70 MPa | 972 psi | ISO 527 |
| Elongation at Break | 390 % | 390 % | ISO 527 |
| Elongation at Yield | 390 % | 390 % | ISO 527 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | ISO D-257 |
| Surface Resistance | <= 1.00e+6 ohm @Thickness 3.00 mm |
<= 1.00e+6 ohm @Thickness 0.118 in |
ISO IEC 61340-5-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 170 °C | 338 °F | Cylinder |
| 210 °C | 410 °F | Die | |
| Zone 2 | 180 °C | 356 °F | Cylinder |
| 210 °C | 410 °F | Die | |
| Zone 3 | 190 °C | 374 °F | Cylinder |
| 210 °C | 410 °F | Die | |
| Zone 4 | 200 °C | 392 °F | Cylinder |
| 210 °C | 410 °F | Die | |
| Zone 5 | 210 °C | 410 °F | Die |
| 210 °C | 410 °F | Cylinder | |
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Roll Temperature | 50.0 °C | 122 °F | 3rd Roll |
| 60.0 °C | 140 °F | 1st Roll | |
| 60.0 °C | 140 °F | 2nd Roll | |
| Drying Temperature | <= 65.0 °C | <= 149 °F | Pre-drying |
| Dry Time | 1 - 3 hour | 1 - 3 hour | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure (psi) | Low-Medium | |
| Injection Speed | Medium-High |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 65 M10 PC/ABS-blend, Reinforced
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 59 Shore A (discontinued **)
- Gromax BFM30-EL03N1 Nylon 6 30% Mineral Filled (Conditioned)
- Saint-Gobain Rulon® 123 Grade Bearing/Seal PTFE
- Zotefoams Plastazote® LD30 Low Density Polyethylene Foam
- Trelleborg Fillite® FG (300) Alumino-silicate Cenospheres
- Dow Corning XIAMETER® PMCPOFX-0536 Fluid
- EMS-Grivory Grivory® LV-3A H PA12-GF30
- DuPont Teijin Films Mylar® M461 Polyester Film, 142 Gauge
- Asahi Glass Fluon® G201 PTFE Granular Powder
Copyright © lookpolymers.com All Rights Reserved