SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP Stat-Kon WCF-1006 is a compound based on PET/PBT resin containing carbon and glass fiber reinforcements.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| 1.51 g/cc | 0.0546 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | Type I, 5 mm/min; ASTM D 638 |
| 141 MPa | 20500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 136 MPa | 19700 psi | Type I, 5 mm/min; ASTM D 638 |
| 141 MPa | 20500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| 211 % | 211 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 |
| 1.8 % | 1.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.96 GPa | 2025 ksi | 1 mm/min; ISO 527 |
| 18.6 GPa | 2700 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 212 MPa | 30700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 211 MPa | 30600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 11.62 GPa | 1685 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.680 J/cm @Temperature 23.0 °C |
1.27 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 6.12 J/cm @Temperature 23.0 °C |
11.5 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 223 °C @Thickness 3.20 mm |
433 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® V 5502 TPE Thermoplastic Polyolefin Elastomer
- Process Technologies Inc Silicone-Clear Sanitary Gasket
- HP Alloys Nitronic® 50 Austenitic Stainless, Level 4 Cold Worked
- Sharadaa Ceramics And Bulk Fiber
- Hexcel® HexPly® EF02 Epoxy Curing System after THR 120 EF01 S50 37% Curing Cycle
- A. Schulman POLYFORT™ FPP 1609 Mica Fortified Copolymer Polypropylene
- Covestro Desmopan® DP 3065D Polyurethane
Copyright © lookpolymers.com All Rights Reserved