SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* WFB54 is a compound based on Polybutylene Terephalate resin containing Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.08 g/cc | 0.0751 lb/in³ | ASTM D792 |
| 2.08 g/cc | 0.0751 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D955 |
| 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
| 66.0 MPa | 9570 psi | ASTM D638 | |
| Elongation at Break | 5.5 % | 5.5 % | ISO 527 |
| 6.0 % | 6.0 % | ASTM D638 | |
| Tensile Modulus | 10.09 GPa | 1463 ksi | 1 mm/min; ISO 527 |
| 15.85 GPa | 2299 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FN-262-S High Strength Nickel Steel Powdered Metal
- Covestro Texin® DP 7-1158 Urethane Thermoplastic Elastomer (discontinued **)
- Resinlab® AR 4305 HP Metal Bonding Methacrylate Adhesive
- Kingfa PA66-G30 30% Glass Fiber Reinforced PA66
- Techmer ES HiFill® TPU 85A 0152 S1
- Styrolution PS 476L HIPS
- Sharadaa Ceramics ZAP 012 Smart Cast Application
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved