Solvay TECHNYL® C 246 V 30 PA6, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 246 V 30 PA6, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced with 30 % of glass fiber, high impact strength, for injection molding.Available in: Asia Pacific and North AmericaProduct Applications: Having good mechanical properties, this grade is used in all sectors of industry. It is suitable for molding of sporting and leisure goods such as roller-skates frames but also for molding of power tools or chainsaws. This product is available in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Water Absorption | 0.95 % @Temperature 23.0 °C, Time 86400 sec |
0.95 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0056 cm/cm | 0.0056 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0044 cm/cm | 0.0044 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0079 cm/cm | 0.0079 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 Type 1A |
| Tensile Modulus | 8.20 GPa | 1190 ksi | ISO 527 Type 1A |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | -30; ISO 179/1eU |
| 8.60 J/cm² | 40.9 ft-lb/in² | 23; ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 225-230°C |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 51 General Purpose Acrylic Resin
- Network Polymers NPP 50-5052
- Kraton® G1643 M (SEBS) Linear Triblock Copolymer
- SolVin 367NC Polyvinyl Chloride Low Viscosity Paste
- Eurotec® Tecodur® PB70 GR15 NL100 PBT, 15% glass fiber reinforced, natural
- 3M Dyneon™ PVDF 2066_0002 Fluoroplastic
- Addiplast Addinyl B2 G10 V20 Nylon 6, Glass/Mineral Filled
- Haynes 242® alloy, hot rolled plate, annealed and aged
- Cosmic Plastics 6160 Mineral Filled Ortho Diallyl Phthalate Molding Compound
Copyright © lookpolymers.com All Rights Reserved