Toyobo GLAMIDE® TY-181GC Nylon/Elastomer
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-181GC Nylon/Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-181GC is a GF reinforced alloy of nylon and elastomer. It has high rigidity and high toughness and contains 43% GF.43
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 43 % | 43 % | |
| Water Absorption | 0.80 % | 0.80 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0030 - 0.0060 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0060 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 84.0 MPa @Temperature 80.0 °C |
12200 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.6%); ASTM-D638 |
| 110 MPa @Temperature 80.0 °C |
16000 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 115 MPa @Temperature 23.0 °C |
16700 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.6%); ASTM-D638 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 240 MPa @Temperature -40.0 °C |
34800 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.6%); ASTM-D638 | |
| 280 MPa @Temperature -40.0 °C |
40600 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.6 % | 3.6 % | Absolute Drying; ASTM-D638 |
| 4.0 % | 4.0 % | Practical Use (Water Absorption 1.6%); ASTM-D638 | |
| Flexural Strength | 87.0 MPa @Temperature 80.0 °C |
12600 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 |
| 130 MPa @Temperature 80.0 °C |
18900 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 | |
| 245 MPa @Temperature 23.0 °C |
35500 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 288 MPa @Temperature -40.0 °C |
41800 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 | |
| 345 MPa @Temperature -40.0 °C |
50000 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 4.00 GPa @Temperature 80.0 °C |
580 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 |
| 5.60 GPa @Temperature 80.0 °C |
812 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 6.00 GPa @Temperature 23.0 °C |
870 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 | |
| 9.80 GPa @Temperature 23.0 °C |
1420 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 11.7 GPa @Temperature -40.0 °C |
1700 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.6%); ASTM-D790 | |
| 13.0 GPa @Temperature -40.0 °C |
1890 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 140 MPa | 20300 psi | Absolute Drying; ASTM-D695 |
| Izod Impact, Notched | 1.70 J/cm @Temperature -40.0 °C |
3.18 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 1.90 J/cm @Temperature -40.0 °C |
3.56 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.6%); ASTM-D256 | |
| 3.25 J/cm @Temperature 23.0 °C |
6.09 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Practical Use (Water Absorption 1.6%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C | 13.3 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 1.6%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 19.0 kV/mm @Thickness 2.00 mm |
483 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.6%); ASTM-D149 |
| 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 83 sec | 83 sec | Practical Use (Water Absorption 1.6%); ASTM-D495 |
| 90 sec | 90 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 575 V | 575 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Injection Pressure | 30.0 - 70.0 MPa | 4350 - 10200 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY HRA222F ASA+PC
- Overview of materials for Polyphthalamide (PPA), Stainless Fiber, EMI
- Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber
- Karina E 880-10/136-A-IS-As White PVC Compound
- DSM Arnitel® EM400 Polyether Ester Elastomer (European and Asian Grade)
- Diamond Polymers ASA/PC TA-35
- Arlon Thermavac® 0.030" (0.762 mm) Uncured Silicone Vacuum Bagging (30400N030)
- Ascend Performance Materials Vydyne® 47 NT Nylon 66, Impact Modified, Conditioned
- Arlon 51986RA020 0.020" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Tipco Tipcolene® FPC 30 PPC - 30% Calcium Carbonate Reinforced Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved