Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 60% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika E-RUNG60 PA66, 60% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039 |
| Tensile Strength at Break | 240 MPa | 34800 psi | ISO 527-1/-2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-1/-2 |
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527-1/-2 |
| Flexural Strength | 370 MPa | 53700 psi | ISO 178 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
Users viewing this material also viewed the following:
- Polymer Resources PC/TP-GP1 PC/Polyester Alloy
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, Hardness 62A
- Industeel SIRIUS 800 H+ Heat Resistant Alloy
- Karina E 813-10/369-BY-ERYB White PVC Compound
- Teknor Apex Monprene® MP-2235 Thermoplastic Elastomer
- A. Schulman FORMION™ FI 243 Ionomer
- A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- DSM Akulon® K223-HGM24 Nylon 6-30% Glass and Mineral Reinforced (European and Asian Grade) (Dry)
- Eurotec® Tecodur® PB70 GR30 NL100 PBT, 20% glass fiber reinforced, natural
- Arlon 42561R006 0.0055" (0.140 mm) Uncured Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved