- Polymer Property : Flexural Strength = 18000 psi
Polymer Property : Flexural Strength = 18000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Premix Premi-Glas® 2103-22 CR-SX-HT Fiberglass Reinforced Thermoset BMC Premi-Glas® 2103-22 CR-SX-HT is a fiberglass reinforced thermoset bulk molding compound for electrical and flame retardant applications.Key features and benefits are:Enhanced product for higher UL .. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Ravago Manufacturing Americas Hylex® P1310G10 HB Polycarbonate, 10% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Gharda Chemicals Gafone™ 3100 Polyethersulfone (PES)
(discontinued **) Characteristics: Excellent Thermal Resistance - Tg 224°C Outstanding Mechanical, Electrical, Flame & Chemical Resistance Very good Hydrolytic & Sterilization Resistance Good Optical Cl.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC (Asia Pacific) LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Flexural Strength | 124 MPa | 18000 psi | |
| Cookson Group Plaskon® 3400 Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A reduced-stress epoxy molding compound for the encapsulation of a variety of semiconductor devices ranging from small lead count.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | |
| Cookson Group Plaskon® 3400FP Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A fast curing, reduced-stress epoxy molding compound for the encapsulation of semiconductor devices including DIPs, PLCCs, SOICs .. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 457 PBT 6.5% GR PBT, UL94 V-0/5V. |
|||
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Valox® 735 PBT 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.This data was supplied by SABIC-IP for the Americas re.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Valox® 735 PBT (Asia Pacific) 40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Techmer ES Plaslube® NY-1/MS/5 NAT PA66 |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 LNP* THERMOCOMP* RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 (Asia Pacific) LNP* Thermocomp* RB006 is a compound based on Nylon 66 resin containing Glass Bead. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| Denka TX-400S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| Ascend Performance Materials Vydyne® R220 Nylon 66, 40% mineral reinforced, DAM Vydyne® R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing adva.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Dry as Molded Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent .. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Applied Composites 8012 Polyester SMC Industry Application: SpecialtyProduct Application: Food EquipmentDistinct Features: NSF ApprovedInformation provided by Applied Composites Corporation. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Asahi Kasei Thermylene® P6-30FG-0860 30% Glass Fiber Reinforced, UV Stabilized Information provided by Asahi Thermofil |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Techmer ES Luriblend® HTN 01410 BK Availability: North AmericaForms: PelletsAdditive: Graphite Powder Lubricant and Molybdenum Disulfide LubricantFeatures: Good Wear Resistance, Low Friction, High Heat Resistance and LubricatedAppear.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000A PC (Europe-Africa-Middle East) LNP* Thermocomp* Lexan_LGN2000A compound is a 20% glass reinforced PC, high flow. UL rated V-0. Consumer Electronics applications. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp MF0069S PP LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi.. |
|||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpir.. |
|||
| Flexural Strength | 124 MPa @Temperature 22.8 °C |
18000 psi @Temperature 73.0 °F |
ASTM D790 |
| Quadrant EPP Duratron® PAI T7530, Compression Molded Carbon Fiber Reinforced Polyamide-Imide |
|||